In this study, H13 tool steel sculptures are built by a metal 3D printing process at various laser scan speeds. The properties of commercial H13 tool steel powders are confirmed for the metal 3D printing process used: powder bed fusion (PBF), which is a selective laser melting (SLM) process. Commercial H13 powder has an excellent flowability of 16.68 s/50 g with a Hausner ratio of 1.25 and a density of 7.68 g/cm³. The sculptures are built with dimensions of 10 × 10 × 10 mm3 in size using commercial H13 tool steel powder. The density measured by the Archimedes method is 7.64 g/cm³, similar to the powder density of 7.68 g/cm³. The hardness is measured by Rockwell hardness equipment 5 times to obtain a mean value of 54.28 HRC. The optimum process conditions in order to build the sculptures are a laser power of 90 W, a layer thickness of 25 μm, an overlap of 30%, and a laser scan speed of 200 mm/s.

Citations

Citations to this article as recorded by  

• Enhancement of resistance to cracking under thermal cycling of EDM-treated H13 steel by shot peening with optimized intensity
  Pengpeng Zuo, Zhiyang Dou, Huikai Yang, Haoyan Hou, Yafeng Zheng
  Engineering Failure Analysis.2026; 187: 110622.     CrossRef
• A Study on Fabrication of PCD Boring Tool Body based on Metal 3D Printing Technology
  Ho Min Son, Dong Gyu Kim, Min-Woo Sa
  Journal of the Korean Society for Precision Engineering.2026; 43(2): 189.     CrossRef
• Plasma nitriding of additively manufactured H13 tool steel for enhanced surface properties
  Samo Tome, Danijela A. Skobir Balantič, Črtomir Donik, Bojan Podgornik, Aleksandra Kocijan, Irena Paulin, Aleš Nagode, Matjaž Godec
  Surface and Coatings Technology.2026; 541: 134062.     CrossRef
• Spheroidization of Enamel Powders by Radio Frequency Plasma Treatment and Application to Additive Manufacturing
  Ki-Bong Kim, Dong-Yeol Yang, Yong-Jin Kim, Jungho Choe, Ji-Na Kwak, Woo-Hyung Jung
  Journal of Korean Powder Metallurgy Institute.2020; 27(5): 388.     CrossRef
• Microstructural effects on the tensile and fracture behavior of selective laser melted H13 tool steel under varying conditions
  Jungsub Lee, Jungho Choe, Junhyeok Park, Ji-Hun Yu, Sangshik Kim, Im Doo Jung, Hyokyung Sung
  Materials Characterization.2019; 155: 109817.     CrossRef
• Nano-mechanical Behavior of H13 Tool Steel Fabricated by a Selective Laser Melting Method
  Van Luong Nguyen, Eun-ah Kim, Jaecheol Yun, Jungho Choe, Dong-yeol Yang, Hak-sung Lee, Chang-woo Lee, Ji-Hun Yu
  Metallurgical and Materials Transactions A.2019; 50(2): 523.     CrossRef
• Correlation between Microstructure and Mechanical Properties of the Additive Manufactured H13 Tool Steel
  Woojin An, Junhyeok Park, Jungsub Lee, Jungho Choe, Im Doo Jung, Ji-Hun Yu, Sangshik Kim, Hyokyung Sung
  Korean Journal of Materials Research.2018; 28(11): 663.     CrossRef
• Evaluation of Strain-Rate Sensitivity of Selective Laser Melted H13 Tool Steel Using Nanoindentation Tests
  Van Luong Nguyen, Eun-ah Kim, Seok-Rok Lee, Jaecheol Yun, Jungho Choe, Dong-yeol Yang, Hak-sung Lee, Chang-woo Lee, Ji-Hun Yu
  Metals.2018; 8(8): 589.     CrossRef
• Comparison of Nano-Mechanical Behavior between Selective Laser Melted SKD61 and H13 Tool Steels
  Jaecheol Yun, Van Luong Nguyen, Jungho Choe, Dong-Yeol Yang, Hak-Sung Lee, Sangsun Yang, Ji-Hun Yu
  Metals.2018; 8(12): 1032.     CrossRef
• A study about sculpture characteristic of SKD61 tool steel fabricated by selective laser melting(SLM) process
  Jaecheol Yun, Jungho Choe, Ki-Bong Kim, Sangsun Yang, Dong-Yeol Yang, Yong-Jin Kim, Chang-Woo Lee, Chang-Woo Lee
  Journal of Korean Powder Metallurgy Institute.2018; 25(2): 137.     CrossRef